| Customization: | Available |
|---|---|
| Application: | Automobile, Construction, Fiber & Garment, Footwear & Leather, Packing, Woodworking, Automobile, Electronic Product |
| Bonding Function: | Structural Adhesive, Potting Adhesive, Sealant |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| test item | Units and conditions | criterion of detection | A / B | |
| surface | A B |
visualization | visualization | Black/white viscous fluid |
| visualization | visualization | Brownish liquid | ||
dynamic viscosity |
A B A+B |
25ºC, mPa·s | GB/T 10247-2008 | 20,000± 10,000 |
| 25ºC, mPa·s | GB/T 10247-2008 | 35±10 | ||
| 25ºC, mPa·s | GB/T 10247-2008 | 2,000±800 | ||
density |
A B A+B |
25ºC, g/cm3 | GB/T 15223-1994 | 1.80±0.05 |
| 25ºC, g/cm3 | GB/T 15223-1994 | 1.23±0.05 | ||
| 25ºC, g/cm3 | GB/T 15223-1994 | 1.75±0.05 | ||
| Operational time | 25ºC min 150g Viscosity to 100000mPa·s |
GB/T 10247-2008 | 60~120 | |
| Gel time | 25ºC hrs 150g | GB/T 10247-2008 | 4~8 | |
| matching | proportion by weight | ---- | A :B=100 :10 | |
| condition of cure | ºC/h | ---- | 25ºC/ 72 h or 70ºC/3h | |
| project | Units or conditions | criterion of detection | JOMP2651 |
| pigment | visualization | visualization | Black or white |
| hardness | Shore D | GB/T 531-2008 | 45±5 |
| water absorption | 24hrs, 25ºC , % | GB 8810-2005 | <0.2 |
| tensile strength | MPa | GB/T 528-2009 | 7.0 |
| elongation | % | GB/T 528-2009 | 50 |
| shear strength | MPa, Fe-Fe | GB/T 6328-86 | 1.5 |
| shear strength | MPa, Al-Al | GB/T 6328-86 | 1.5 |
| thermal conductivity | W/m.K | GB/T10297-1998 | 1.30 |
| Glass transition temperature Tg | ºC | GBT 11998-1989 | 10 |
| mass resistivity | 25ºC , Ω·cm | GB/T 1692-92 | 1.5*1014 |
| insulation strength | 25ºC , kV/mm | GB/T 1695-2005 | 18 |
| dielectric constant | 50Hz ,25ºC | GB/T 1693-2007 | 4.50 |
| dielectric loss | 50Hz ,25ºC | GB/T 1693-2007 | 0.012 |
| line shrinkage | % | HGT 2625-1994 | 1.0 |
| linear thermal expansion | μm/( m ,ºC ) | GBT 20673-2006 | <Tg, 35 >Tg, 120 |
| Application temperature | ºC | GBT 20028-2005 | -50~130 |
| Flame retardant rating | UL | UL94 | V-0 |
| type | model number | Product Description | Color | Mix ratio (By weight) | Viscosity | Pot life 25ºC min,150g | Initial curing time 25ºC, 55%RH,hr | Complete curing time | Hardness | Thermal conductivity | Usage temperature |
| Polyurethane structural adhesive | JOMP 2103 | High strength bonding with high toughness | black | 1:1 | 20000CPS | 10~20min | 30min | 24h-48h | 60D | 0.3w | -50~100ºC |
| JOMP 2650 | 2.0W high thermal conductivity, high strength | green | 1:1 | 150000cps | 30~50min | 60~120min | 24h-48h | 75D | 2.0w | -50~100ºC | |
| JOMP 2101 | High strength bonding, specific fluidity | black | 1:1 | 10000CPS | 20~30min | 40~60min | 24h-48h | 70D | 0.3w | -50~100ºC |